Best Polycarbonate Best Polycarbonate Best Polycarbonate
Polycarbonate Tube 12/10
Discover the excellence of our Polycarbonate Tubes, offering top-tier quality, exceptional performance, and unmatched durability, making them the clearest extruded tubes available today. These tubes are renowned for their flawless optical clarity and a surface free from any imperfections.
Our Polycarbonate Tubes are known for their optical purity, finding application in a variety of sectors, including stand and exhibition construction, furniture and interior design, and technical uses like reactors.
While our Polycarbonate Tubes are UV-stable and weather-resistant, please note that they are not intended for prolonged outdoor use, as extended exposure may cause them to yellow over time.
In the realm of architectural lighting, our Polycarbonate Tubes open the door to high-quality, design-oriented applications. With our Satin Frost Polycarbonate Tubes, you can effortlessly create stunning lighting effects. This innovative solution is particularly suitable for lighting and architectural applications, with white or frosted satin finishes providing superb diffused lighting and a soft, glare-free surface.
Working with Polycarbonate Tubes is straightforward when using the right tools. However, it’s crucial to maintain high cutting speeds and effective cooling to prevent overheating and localized thermal stress, as Polycarbonate’s low heat conduction can lead to these issues.
Excessive friction, especially with Polycarbonate Tubes, may result in melting, leading to a sticky surface and difficulties in machining. When drilling, always make sure to use a water-based cooling lubricant, such as an emulsion. In some cases, annealing may be required to eliminate internal stress.
Mechanical Properties
| MECHANICAL PROPERTIES | VALUE | UNIT | PARAMETER | NORM |
|---|---|---|---|---|
| Tensile strength | 69 | MPa | 50mm/min | DIN EN ISO 527-2 |
| Tensile strength at yield | 69 | MPa | 50mm/min | DIN EN ISO 527-2 |
| Elongation at yield | 6 | % | 50mm/min | DIN EN ISO 527-2 |
| Elongation at break | 90 | % | 50mm/min | DIN EN ISO 527-2 |
| Flexural strength | 97 | MPa | 2mm/min, 10 N | DIN EN ISO 178 |
| Modulus of elasticity (flexural test) |
2300 | MPa | 2mm/min, 10 N | DIN EN ISO 178 |
| Compression strength | 16/29/64 | MPa | 1% / 2% / 5% | EN ISO 604 |
| Compression modulus | 2000 | MPa | 5mm/min, 10 N | EN ISO 604 |
| Impact strength (Charpy) | n.b. | kJ/m2 | max. 7,5J | DIN EN ISO 179-1eU |
| Notched impact strength (Charpy) | 14 | kJ/m2 | max. 7,5J | DIN EN ISO 179-1eA |
| Ball indentation hardness | 128 | MPa | ISO 2039-1 | |
| Modulus of elasticity (tensile test) |
2200 | MPa | 1mm/min | DIN EN ISO 527-2 |
Thermal Properties
| THERMAL PROPERTIES | VALUE | UNIT | PARAMETER | NORM |
|---|---|---|---|---|
| Melting temperature | n.a. | C | DIN EN ISO 11357 | |
| Service temperature | 140 | C | short term | NN |
| Service temperature | 120 | C | long term | NN |
| Thermal expansion (CLTE) | 8 | 10-5*1/K | 23-60°C, long. | DIN EN ISO 11359-1;2 |
| Thermal expansion (CLTE) | 8 | 10-5*1/K | 23-100°C, long. | DIN EN ISO 11359-1;2 |
| Glass transition temperature | 149 | C | DIN EN ISO 11357 | |
| Thermal conductivity | 0.25 | W/(k*m) | ISO 22007-4:2008 | |
| Specific heat | 1.3 | J/(g*K) | ISO 22007-4:2008 |
Electrical Properties
| ELECTRICAL PROPERTIES | VALUE | UNIT | PARAMETER | NORM |
|---|---|---|---|---|
| surface resistivity | 1014 | O | DIN IEC 60093 | |
| volume resistivity | 1014 | O*cm | DIN IEC 60093 |
Other Properties
| OTHER PROPERTIES | VALUE | UNIT | PARAMETER | NORM |
|---|---|---|---|---|
| Resistance to hot water/ bases | – | – | – | |
| Resistance to weathering | (+) | – | – | |
| Flammability (UL94) | HB | – | listed (value at 0.4 and 1.5 mm) | DIN IEC 60695-11-10; |
| Water absorption | 0.06 | % | 24h / 96h (23°C) | DIN EN ISO 62 |