Polycarbonate Tube 25/22 Polycarbonate Tube 25/22 Polycarbonate Tube 25/22
Polycarbonate Tubes for Versatile Applications
Our Polycarbonate Tube 25/22 offers exceptional clarity and performance, making it a top choice for various applications. These tubes are renowned for their flawless optics and smooth, striation-free surface.
Polycarbonate tubes are optically clear, making them ideal for a wide range of uses, including stand and showcase construction, furniture and interior design, and technological applications like reactors.
While Polycarbonate Tubes are UV stable and weatherproof, please note that they are not suitable for prolonged outdoor exposure as they may yellow over time.
In the architectural lighting industry, our Polycarbonate Tubes shine, allowing you to craft impressive lighting effects. Our Satin Frost Polycarbonate Tubes offer an innovative solution for lighting and architectural applications, with white or frosted satin finishes that provide excellent diffused light, creating a velvety, non-glare surface.
Working with Polycarbonate Tubes is easy with the right tools. Ensure high cutting speeds and effective cooling to prevent overheating and local thermal stress. Excessive friction, especially when machining Polycarbonate Tubes, can result in melting and a sticky surface. When drilling, always use water-based cooling lubricant (e.g., an emulsion). Additionally, annealing may be necessary to eliminate internal stress.
Mechanical Properties
| MECHANICAL PROPERTIES | VALUE | UNIT | PARAMETER | NORM |
|---|---|---|---|---|
| Tensile strength | 69 | MPa | 50mm/min | DIN EN ISO 527-2 |
| Tensile strength at yield | 69 | MPa | 50mm/min | DIN EN ISO 527-2 |
| Elongation at yield | 6 | % | 50mm/min | DIN EN ISO 527-2 |
| Elongation at break | 90 | % | 50mm/min | DIN EN ISO 527-2 |
| Flexural strength | 97 | MPa | 2mm/min, 10 N | DIN EN ISO 178 |
| Modulus of elasticity (flexural test) |
2300 | MPa | 2mm/min, 10 N | DIN EN ISO 178 |
| Compression strength | 16/29/64 | MPa | 1% / 2% / 5% | EN ISO 604 |
| Compression modulus | 2000 | MPa | 5mm/min, 10 N | EN ISO 604 |
| Impact strength (Charpy) | n.b. | kJ/m2 | max. 7,5J | DIN EN ISO 179-1eU |
| Notched impact strength (Charpy) | 14 | kJ/m2 | max. 7,5J | DIN EN ISO 179-1eA |
| Ball indentation hardness | 128 | MPa | ISO 2039-1 | |
| Modulus of elasticity (tensile test) |
2200 | MPa | 1mm/min | DIN EN ISO 527-2 |
Thermal Properties
| THERMAL PROPERTIES | VALUE | UNIT | PARAMETER | NORM |
|---|---|---|---|---|
| Melting temperature | n.a. | C | DIN EN ISO 11357 | |
| Service temperature | 140 | C | short term | NN |
| Service temperature | 120 | C | long term | NN |
| Thermal expansion (CLTE) | 8 | 10-5*1/K | 23-60°C, long. | DIN EN ISO 11359-1;2 |
| Thermal expansion (CLTE) | 8 | 10-5*1/K | 23-100°C, long. | DIN EN ISO 11359-1;2 |
| Glass transition temperature | 149 | C | DIN EN ISO 11357 | |
| Thermal conductivity | 0.25 | W/(k*m) | ISO 22007-4:2008 | |
| Specific heat | 1.3 | J/(g*K) | ISO 22007-4:2008 |
Electrical Properties
| ELECTRICAL PROPERTIES | VALUE | UNIT | PARAMETER | NORM |
|---|---|---|---|---|
| surface resistivity | 1014 | O | DIN IEC 60093 | |
| volume resistivity | 1014 | O*cm | DIN IEC 60093 |
Other Properties
| OTHER PROPERTIES | VALUE | UNIT | PARAMETER | NORM |
|---|---|---|---|---|
| Resistance to hot water/ bases | – | – | – | |
| Resistance to weathering | (+) | – | – | |
| Flammability (UL94) | HB | – | listed (value at 0.4 and 1.5 mm) | DIN IEC 60695-11-10; |
| Water absorption | 0.06 | % | 24h / 96h (23°C) | DIN EN ISO 62 |