Polycarbonate Tube Polycarbonate Tube Polycarbonate Tube
Polycarbonate Tube 30/24
Our Polycarbonate Tubes stand out as the top choice for exceptional clarity, superior performance, and long-lasting durability in the extruded tube market. These tubes are renowned for their flawless optics, boasting a perfectly smooth surface that’s free from any imperfections.
Polycarbonate tubes are optically clear, making them ideal for a wide range of applications. They find their place in stand and showcase constructions, various furniture and interior design projects, and even technological applications such as reactors.
While Polycarbonate Tubes are UV stable and weather-resistant, it’s important to note that they are not intended for prolonged outdoor use, as extended exposure to the elements may cause them to develop a yellow tint.
For the architectural lighting industry, our Polycarbonate Tubes offer endless possibilities. Achieve stunning lighting effects with our Satin Frost Polycarbonate Tubes, a revolutionary solution perfect for lighting and architectural applications. The white or frosted satin finishes create a beautifully diffused light, resulting in a velvety, non-glare surface.
Working with Polycarbonate Tubes is manageable with the right tools. However, it’s crucial to use high cutting speeds and effective cooling to prevent overheating and local thermal stress. Excessive friction, particularly with Polycarbonate Tubes, can lead to melting and result in a tacky surface, making machining difficult. When drilling, always use a water-based cooling lubricant (such as an emulsion) to prevent these issues. In some cases, annealing may be required to eliminate internal stress.
Mechanical Properties
| MECHANICAL PROPERTIES | VALUE | UNIT | PARAMETER | NORM |
|---|---|---|---|---|
| Tensile strength | 69 | MPa | 50mm/min | DIN EN ISO 527-2 |
| Tensile strength at yield | 69 | MPa | 50mm/min | DIN EN ISO 527-2 |
| Elongation at yield | 6 | % | 50mm/min | DIN EN ISO 527-2 |
| Elongation at break | 90 | % | 50mm/min | DIN EN ISO 527-2 |
| Flexural strength | 97 | MPa | 2mm/min, 10 N | DIN EN ISO 178 |
| Modulus of elasticity (flexural test) |
2300 | MPa | 2mm/min, 10 N | DIN EN ISO 178 |
| Compression strength | 16/29/64 | MPa | 1% / 2% / 5% | EN ISO 604 |
| Compression modulus | 2000 | MPa | 5mm/min, 10 N | EN ISO 604 |
| Impact strength (Charpy) | n.b. | kJ/m2 | max. 7,5J | DIN EN ISO 179-1eU |
| Notched impact strength (Charpy) | 14 | kJ/m2 | max. 7,5J | DIN EN ISO 179-1eA |
| Ball indentation hardness | 128 | MPa | ISO 2039-1 | |
| Modulus of elasticity (tensile test) |
2200 | MPa | 1mm/min | DIN EN ISO 527-2 |
Thermal Properties
| THERMAL PROPERTIES | VALUE | UNIT | PARAMETER | NORM |
|---|---|---|---|---|
| Melting temperature | n.a. | C | DIN EN ISO 11357 | |
| Service temperature | 140 | C | short term | NN |
| Service temperature | 120 | C | long term | NN |
| Thermal expansion (CLTE) | 8 | 10-5*1/K | 23-60°C, long. | DIN EN ISO 11359-1;2 |
| Thermal expansion (CLTE) | 8 | 10-5*1/K | 23-100°C, long. | DIN EN ISO 11359-1;2 |
| Glass transition temperature | 149 | C | DIN EN ISO 11357 | |
| Thermal conductivity | 0.25 | W/(k*m) | ISO 22007-4:2008 | |
| Specific heat | 1.3 | J/(g*K) | ISO 22007-4:2008 |
Electrical Properties
| ELECTRICAL PROPERTIES | VALUE | UNIT | PARAMETER | NORM |
|---|---|---|---|---|
| surface resistivity | 1014 | O | DIN IEC 60093 | |
| volume resistivity | 1014 | O*cm | DIN IEC 60093 |
Other Properties
| OTHER PROPERTIES | VALUE | UNIT | PARAMETER | NORM |
|---|---|---|---|---|
| Resistance to hot water/ bases | – | – | – | |
| Resistance to weathering | (+) | – | – | |
| Flammability (UL94) | HB | – | listed (value at 0.4 and 1.5 mm) | DIN IEC 60695-11-10; |
| Water absorption | 0.06 | % | 24h / 96h (23°C) | DIN EN ISO 62 |