Best Polycarbonate Tube Best Polycarbonate Tube Best Polycarbonate Tube
Polycarbonate Tubes: The Pinnacle of Clarity
Our Polycarbonate Tubes stand out as the clearest extruded tubes available, promising top-notch quality, exceptional performance, and remarkable durability. They exhibit pristine optics and a flawlessly smooth surface devoid of any imperfections.
These optically clear Polycarbonate Tubes find utility in a variety of applications, including stand and showcase constructions, furniture and interior design, as well as technological uses like reactors. While they offer excellent UV stability and weather resistance, it’s important to note that they aren’t intended for prolonged outdoor exposure, as extended exposure can result in yellowing.
For those involved in architectural lighting, our Polycarbonate Tubes offer endless creative possibilities. Our Satin Frost Polycarbonate Tubes, specifically tailored for lighting and architectural applications, enable you to craft striking lighting effects. With white or frosted satin finishes, they disperse light excellently, creating a smooth, glare-free surface.
Working with Polycarbonate Tubes is a manageable task with the right tools at hand. High cutting speeds and effective cooling are essential, as the low heat conduction of these tubes makes them susceptible to overheating and localized thermal stress. Excessive friction, especially during machining, can lead to melting and the formation of a sticky surface. When drilling, always employ a water-based cooling lubricant (such as an emulsion). In some cases, annealing might be necessary to eliminate internal stress.
Mechanical Properties
| MECHANICAL PROPERTIES | VALUE | UNIT | PARAMETER | NORM |
|---|---|---|---|---|
| Tensile strength | 69 | MPa | 50mm/min | DIN EN ISO 527-2 |
| Tensile strength at yield | 69 | MPa | 50mm/min | DIN EN ISO 527-2 |
| Elongation at yield | 6 | % | 50mm/min | DIN EN ISO 527-2 |
| Elongation at break | 90 | % | 50mm/min | DIN EN ISO 527-2 |
| Flexural strength | 97 | MPa | 2mm/min, 10 N | DIN EN ISO 178 |
| Modulus of elasticity (flexural test) |
2300 | MPa | 2mm/min, 10 N | DIN EN ISO 178 |
| Compression strength | 16/29/64 | MPa | 1% / 2% / 5% | EN ISO 604 |
| Compression modulus | 2000 | MPa | 5mm/min, 10 N | EN ISO 604 |
| Impact strength (Charpy) | n.b. | kJ/m2 | max. 7,5J | DIN EN ISO 179-1eU |
| Notched impact strength (Charpy) | 14 | kJ/m2 | max. 7,5J | DIN EN ISO 179-1eA |
| Ball indentation hardness | 128 | MPa | ISO 2039-1 | |
| Modulus of elasticity (tensile test) |
2200 | MPa | 1mm/min | DIN EN ISO 527-2 |
Thermal Properties
| THERMAL PROPERTIES | VALUE | UNIT | PARAMETER | NORM |
|---|---|---|---|---|
| Melting temperature | n.a. | C | DIN EN ISO 11357 | |
| Service temperature | 140 | C | short term | NN |
| Service temperature | 120 | C | long term | NN |
| Thermal expansion (CLTE) | 8 | 10-5*1/K | 23-60°C, long. | DIN EN ISO 11359-1;2 |
| Thermal expansion (CLTE) | 8 | 10-5*1/K | 23-100°C, long. | DIN EN ISO 11359-1;2 |
| Glass transition temperature | 149 | C | DIN EN ISO 11357 | |
| Thermal conductivity | 0.25 | W/(k*m) | ISO 22007-4:2008 | |
| Specific heat | 1.3 | J/(g*K) | ISO 22007-4:2008 |
Electrical Properties
| ELECTRICAL PROPERTIES | VALUE | UNIT | PARAMETER | NORM |
|---|---|---|---|---|
| surface resistivity | 1014 | O | DIN IEC 60093 | |
| volume resistivity | 1014 | O*cm | DIN IEC 60093 |
Other Properties
| OTHER PROPERTIES | VALUE | UNIT | PARAMETER | NORM |
|---|---|---|---|---|
| Resistance to hot water/ bases | – | – | – | |
| Resistance to weathering | (+) | – | – | |
| Flammability (UL94) | HB | – | listed (value at 0.4 and 1.5 mm) | DIN IEC 60695-11-10; |
| Water absorption | 0.06 | % | 24h / 96h (23°C) | DIN EN ISO 62 |