PC / Polycarbonate Rod
Our Extruded Polycarbonate Clear Rod is a top-performing, amorphous thermoplastic boasting impressive characteristics such as outstanding dimensional stability, minimal moisture absorption, and exceptional rigidity. It serves well in temperatures ranging from -40°C to 115°C for long-term use and can handle short-term maximum service temperatures of up to 140°C.
Polycarbonate Engineering Grade Rod finds its applications in various sectors, including the electrical and electronic industries, safety engineering, and vehicle construction. This material is particularly suitable for billeting, precision grinding, and CNC turning.
Please note that Engineering Grade Polycarbonate may not be optically clear and should be chosen for its technical and mechanical attributes rather than aesthetic qualities.
Explore similar materials from our range, such as Acrylic Cast Clear Rod and Acetal C Extruded Natural Rod. If you need machined or finished components made from Polycarbonate Engineering Grade, feel free to contact our team for further details.
Key Features:
- Amorphous Thermoplastic
- Exceptional high impact strength across a broad temperature range
- Impressive combination of toughness, heat and flame resistance, and dimensional stability
- Outstanding impact resistance
- Continuous use temperature up to 290°F (145°C)
- Good transparency
- Excellent thermal performance
- Strong dielectric properties
- Reliable mechanical and electrical properties
- FDA Compliant
- Resistant to acids
- Low moisture absorption rate
We hope this information helps you find the right material for your specific needs.
Mechanical Properties
| MECHANICAL PROPERTIES | VALUE | UNIT | PARAMETER | NORM |
|---|---|---|---|---|
| Tensile strength | 69 | MPa | 50mm/min | DIN EN ISO 527-2 |
| Tensile strength at yield | 69 | MPa | 50mm/min | DIN EN ISO 527-2 |
| Elongation at yield | 6 | % | 50mm/min | DIN EN ISO 527-2 |
| Elongation at break | 90 | % | 50mm/min | DIN EN ISO 527-2 |
| Flexural strength | 97 | MPa | 2mm/min, 10 N | DIN EN ISO 178 |
| Modulus of elasticity (flexural test) |
2300 | MPa | 2mm/min, 10 N | DIN EN ISO 178 |
| Compression strength | 16/29/64 | MPa | 1% / 2% / 5% | EN ISO 604 |
| Compression modulus | 2000 | MPa | 5mm/min, 10 N | EN ISO 604 |
| Impact strength (Charpy) | n.b. | kJ/m2 | max. 7,5J | DIN EN ISO 179-1eU |
| Notched impact strength (Charpy) | 14 | kJ/m2 | max. 7,5J | DIN EN ISO 179-1eA |
| Ball indentation hardness | 128 | MPa | ISO 2039-1 | |
| Modulus of elasticity (tensile test) |
2200 | MPa | 1mm/min | DIN EN ISO 527-2 |
Thermal Properties
| THERMAL PROPERTIES | VALUE | UNIT | PARAMETER | NORM |
|---|---|---|---|---|
| Melting temperature | n.a. | C | DIN EN ISO 11357 | |
| Service temperature | 140 | C | short term | NN |
| Service temperature | 120 | C | long term | NN |
| Thermal expansion (CLTE) | 8 | 10-5*1/K | 23-60°C, long. | DIN EN ISO 11359-1;2 |
| Thermal expansion (CLTE) | 8 | 10-5*1/K | 23-100°C, long. | DIN EN ISO 11359-1;2 |
| Glass transition temperature | 149 | C | DIN EN ISO 11357 | |
| Thermal conductivity | 0.25 | W/(k*m) | ISO 22007-4:2008 | |
| Specific heat | 1.3 | J/(g*K) | ISO 22007-4:2008 |
Electrical Properties
| ELECTRICAL PROPERTIES | VALUE | UNIT | PARAMETER | NORM |
|---|---|---|---|---|
| surface resistivity | 1014 | O | DIN IEC 60093 | |
| volume resistivity | 1014 | O*cm | DIN IEC 60093 |
Other Properties
| OTHER PROPERTIES | VALUE | UNIT | PARAMETER | NORM |
|---|---|---|---|---|
| Resistance to hot water/ bases | – | – | – | |
| Resistance to weathering | (+) | – | – | |
| Flammability (UL94) | HB | – | listed (value at 0.4 and 1.5 mm) | DIN IEC 60695-11-10; |
| Water absorption | 0.06 | % | 24h / 96h (23°C) | DIN EN ISO 62 |